复合无机盐相变蓄冷材料的制备与改性研究

李梦欣; 陈鹏; 吕钟灵; 陈振乾

doi:10.3969/j.issn.0253-4339.2021.04.106

您当前的位置：

首页 >

文章列表页 >

复合无机盐相变蓄冷材料的制备与改性研究

更新时间：2024-07-18

- 复合无机盐相变蓄冷材料的制备与改性研究
- Preparation and Modification of Composite Inorganic Salt Phase Change Materials for Cold Storage
- 制冷学报 2021年42卷第4期
- 作者机构：
  
  1. 东南大学能源与环境学院
  2. 华设设计集团股份有限公司
- 作者简介：
- 基金信息：
  
  华设设计集团股份有限公司开放基金项目（8503008464）资助。
- DOI：10.3969/j.issn.0253-4339.2021.04.106
  中图分类号：
- 纸质出版日期：2021
- 稿件说明：
移动端阅览
李梦欣, 陈鹏, 吕钟灵, 等. 复合无机盐相变蓄冷材料的制备与改性研究[J]. 制冷学报, 2021,42(4).

Li Mengxin, Chen Peng, L, et al. Preparation and Modification of Composite Inorganic Salt Phase Change Materials for Cold Storage[J]. Journal of refrigeration, 2021, 42(4).
李梦欣, 陈鹏, 吕钟灵, 等. 复合无机盐相变蓄冷材料的制备与改性研究[J]. 制冷学报, 2021,42(4). DOI： 10.3969/j.issn.0253-4339.2021.04.106.

Li Mengxin, Chen Peng, L, et al. Preparation and Modification of Composite Inorganic Salt Phase Change Materials for Cold Storage[J]. Journal of refrigeration, 2021, 42(4). DOI： 10.3969/j.issn.0253-4339.2021.04.106.

摘要

针对建筑空调领域6~7 ℃的蓄冷温度要求，本文制备出一种以Na2SO4?10H2O和Na2HPO4?12H2O为蓄冷基底材料的复合无机盐相变材料。通过步冷曲线分析法、差示扫描量热法、瞬态平面热源法等实验方法研究不同种类、质量添加剂对复合无机盐体系的影响。实验结果表明：改性后的复合无机盐体系最终配比为32%Na2SO4?10H2O+48%Na2HPO4?12H2O+ 16%NH4Cl+1.6%硼砂+1.6%CMC+0.8%纳米TiO2，相变温度为6.1~6.3 ℃，相变潜热为130~139 J/g，过冷度低于0.5 ℃，无相分离现象，液相导热系数为0.798 9 W/(m?K)，经过50次循环后，具有良好的热稳定性。

Abstract

Aiming at the temperature requirement of 6–7 ℃ in the field of building air conditioning cold storage

a composite inorganic salt phase change material was prepared with Na2SO4?10H2O and Na2HPO4?12H2O as cold storage base materials. The effects of different types and quality additives on the composite inorganic salt system were studied by step cooling curve analysis

differential scanning calorimetry

and the transient plane heat source method. The experimental results show that the final ratio of the modified composite inorganic salt system is 32% Na2SO4?10H2O + 48% Na2HPO4?12H2O + 16% NH4Cl + 1.6% borax + 1.6%CMC + 0.8%nano-TiO2. The phase transformation temperature is 6.1~6.3 ℃. The latent heat of the phase transformation was 130–139 J/g. The undercooling is less than 0.5 ℃

and no phase separation phenomenon exists. The liquid-phase thermal conductivity is 0.798 9 W/(m?K). After 50 cycles

the composite inorganic salt system exhibits good thermal stability.

关键词

Keywords

references

浏览量

1597

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

填充相变材料的复合搁架的传热与蓄冷特性研究

月桂酸-癸酸/十四醇-十二烷复合相变储能材料的制备与性能研究

有机相变蓄冷材料的研究进展

相变窗传热特性实验研究

空调蓄冷用相变材料的研究进展