Preparation and Modification of Composite Inorganic Salt Phase Change Materials for Cold Storage

Li Mengxin; Chen Peng; L; Zhongling

doi:10.3969/j.issn.0253-4339.2021.04.106

您当前的位置：

首页 >

文章列表页 >

Preparation and Modification of Composite Inorganic Salt Phase Change Materials for Cold Storage

更新时间：2024-07-18

- Preparation and Modification of Composite Inorganic Salt Phase Change Materials for Cold Storage
- Journal of Refrigeration Vol. 42, Issue 4, (2021)
- 作者机构：
  
  1. 东南大学能源与环境学院
  2. 华设设计集团股份有限公司
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0253-4339.2021.04.106
  CLC：
- Published：2021
- 稿件说明：
移动端阅览
Li Mengxin, Chen Peng, L, et al. Preparation and Modification of Composite Inorganic Salt Phase Change Materials for Cold Storage[J]. Journal of refrigeration, 2021, 42(4).
DOI：

Li Mengxin, Chen Peng, L, et al. Preparation and Modification of Composite Inorganic Salt Phase Change Materials for Cold Storage[J]. Journal of refrigeration, 2021, 42(4). DOI： 10.3969/j.issn.0253-4339.2021.04.106.

摘要

针对建筑空调领域6~7 ℃的蓄冷温度要求，本文制备出一种以Na2SO4?10H2O和Na2HPO4?12H2O为蓄冷基底材料的复合无机盐相变材料。通过步冷曲线分析法、差示扫描量热法、瞬态平面热源法等实验方法研究不同种类、质量添加剂对复合无机盐体系的影响。实验结果表明：改性后的复合无机盐体系最终配比为32%Na2SO4?10H2O+48%Na2HPO4?12H2O+ 16%NH4Cl+1.6%硼砂+1.6%CMC+0.8%纳米TiO2，相变温度为6.1~6.3 ℃，相变潜热为130~139 J/g，过冷度低于0.5 ℃，无相分离现象，液相导热系数为0.798 9 W/(m?K)，经过50次循环后，具有良好的热稳定性。

Abstract

Aiming at the temperature requirement of 6–7 ℃ in the field of building air conditioning cold storage

a composite inorganic salt phase change material was prepared with Na2SO4?10H2O and Na2HPO4?12H2O as cold storage base materials. The effects of different types and quality additives on the composite inorganic salt system were studied by step cooling curve analysis

differential scanning calorimetry

and the transient plane heat source method. The experimental results show that the final ratio of the modified composite inorganic salt system is 32% Na2SO4?10H2O + 48% Na2HPO4?12H2O + 16% NH4Cl + 1.6% borax + 1.6%CMC + 0.8%nano-TiO2. The phase transformation temperature is 6.1~6.3 ℃. The latent heat of the phase transformation was 130–139 J/g. The undercooling is less than 0.5 ℃

and no phase separation phenomenon exists. The liquid-phase thermal conductivity is 0.798 9 W/(m?K). After 50 cycles

the composite inorganic salt system exhibits good thermal stability.

关键词

Keywords

references

Views

1597

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Investigation of the Heat Transfer and Cool Storage Characteristic of Composite Shelf Filled With Phase Change Materials

Preparation and Properties of Lauric Acid-decanoic/Tetradecyl Alcohol-dodecane Composite as PCMs for Thermal Energy Storage

Research and Development of Organic Phase Change Materials for Cool Thermal Energy Storage

Experimental Study on Heat Transfer of PCM-filled Window

Research Progress of Phase Change Materials for Cold Thermal Energy Storage in Air-conditioners

Related Author

Yanli

Zhao Xinli

Wang Lixun

Li Weiping

Wu Xuehong

Xu Weiwen

Ding Jinhong

Related Institution

School of Energy and Power Engineering, Zhengzhou University of Light Industry

Institute of Cooling Energy Storage Technology, Shanghai Maritime University

College of Civil Engineering, Guangzhou University

苏州科技大学环境科学与工程学院，

苏州科技大学环境科学与工程学院

Address：10/F, Yindu Mansion, 67 Fucheng Road, Haidian Dist, Beijing, China Postal code：100142
Tel：010-68711412 Email：editor@car.org.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09064830号-19 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰