Heat Transfer Enhancement of a New Composite Adsorbent

Lu Zhenneng; Bu Xianbiao; Wang Lingbao; Ma Weibin

doi:10.3969/j.issn.0253-4339.2013.03.031

您当前的位置：

首页 >

文章列表页 >

Heat Transfer Enhancement of a New Composite Adsorbent

更新时间：2024-07-18

- Heat Transfer Enhancement of a New Composite Adsorbent
- Journal of Refrigeration Vol. 34, Issue 3, (2013)
- 作者机构：
  
  1. 中国科学院广州能源研究所中国科学院可再生能源与天然气水合物重点实验室,中国科学院研究生院
  2. 中国科学院广州能源研究所中国科学院可再生能源与天然气水合物重点实验室
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0253-4339.2013.03.031
  CLC：
- Published：2013
- 稿件说明：
移动端阅览
Lu Zhenneng, Bu Xianbiao, Wang Lingbao, et al. Heat Transfer Enhancement of a New Composite Adsorbent[J]. Journal of refrigeration, 2013, 34(3).
DOI：

Lu Zhenneng, Bu Xianbiao, Wang Lingbao, et al. Heat Transfer Enhancement of a New Composite Adsorbent[J]. Journal of refrigeration, 2013, 34(3). DOI： 10.3969/j.issn.0253-4339.2013.03.031.

摘要

以氯化钙和杉木屑为原料，通过炭化活化的方法制备具有发达孔隙结构的吸附剂，然后加入膨胀石墨以强化吸附剂的传热性能。石墨的含量从0%到50%变化，通过氨吸附性能实验考察石墨含量对吸附量和吸附速率的影响。实验结果表明，在四个小时内，复合吸附剂对氨气的吸附量随着膨胀石墨含量的增加而减小，吸附速率随膨胀石墨含量的增加先增加后减小，而导热系数随膨胀石墨含量的增加单调的增加。对吸附制冷而言，膨胀石墨含量为30%的复合吸附剂具有最佳性能，其导热系数达到0.193W/(m?K)，吸附时间为15 min时对应的吸附量达到0.431 g/g。

Abstract

Composite adsorbents of CaCl2/ activated carbon were prepared by charring and activating at high temperature from CaCl2 and fir crumbs. Thermal conductivity was improved by adding expanded graphite into composite adsorbent. The proportion of expanded graphite in composite adsorbents was changed from 0% to 50%. The effect of the proportion of expanded graphite in composite adsorbents on the uptake and the adsorption rate was observed from ammonia adsorption experiment. It is found that the adsorption capacity of composite absorbent is decreasing all the time while the adsorption rate increasing at first but then decreasing with the increase of the proportion of expanded graphite. It is also found that thermal conductivity of the composite adsorbent is improving with the increase of the proportion of expanded graphite. When the proportion of expanded graphite in composite adsorbent is 30%

the composite adsorbent has the optimum performance for adsorption refrigeration—its thermal conductivity of the composite adsorbent is 0.193 W/(m?K) and its uptake is 0.431 g/g in first 15min of the adsorption time.

关键词

Keywords

references

Views

1988

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effects of CaCl2 Impregnation and Graphene Blending on Adsorption Refrigeration with Activated Carbon-Methanol Working Pair

Evolution of Pressure and Temperature During Start-up Process in U-Shaped Gravity Heat Pipe

Study on the Thermal Conductivity and Permeability of Composite SrCl2-NH3 Working Pair under the Condition of Different Values for Adsorption Quantity

Related Author

Gong Xujin

Wang Junzhu

Dong Yuqi

Li Hailong

Zhang Zhongyao

Li Xueqiang

Liu Shengchun

Zhao Xiaohan

Related Institution

School of Energy and Civil Engineering, Harbin University of Commerce

Key Laboratory of Efficient Utilization of Low and Medium Grade Energy, Tianjin University

Key Laboratory of Refrigeration Technology of Tianjin, Tianjin University of Commerce

天津商业大学

哈尔滨商业大学能源与建筑工程学院

Address：10/F, Yindu Mansion, 67 Fucheng Road, Haidian Dist, Beijing, China Postal code：100142
Tel：010-68711412 Email：editor@car.org.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09064830号-19 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰